Part 1 — SECTION 13. METALLIC OXIDES. (continued 2)

The characters of this oxide are, its olive brown colour, its insolubility in nitric and sulphuric acids, without heat or deoxidation, and its solubility in muriatic acid after the evolution of oxymuriatic acid. By long exposure to the air, it is gradually changed, in all probability into the black oxide.

3. Deutoxide. In order to determine the quantity of oxygen deducible from the purest native oxide of manganese, to convert it into protoxide, I have successfully adopted the two following methods. 1st. Let 39 or 40 grains of the oxide be mixed with 60 common salt; to this add 80 grains of water, and 120 grains weight of strong sulphuric acid, in a gas bottle. The heat must be gradually raised to boiling, and the oxymuriatic acid gas may be received in a quart of lime water. This will be found sufficient to convert 800 measures of test green sulphate of iron (1.156) into red; that is, it will produce 29 grains of oxymuriatic acid, which will cause 7 grains of oxygen, to unite to the green oxide of iron. Now 100 measures of 1.156 sulphate, according to some recent experiments of mine, contain 8 grains of green oxide, (I estimated the sp. gr. of test sulphate, heretofore at 1.149); hence 800 contain 64 oxide, and these require just 7 grains of oxygen to be united to them, to form the red oxide, as has been shewn, page 34. In the above experiment, the 39 grains of oxide, will be found to vanish or be dissolved, if pure, and to yield 32 grains of protoxide, making up with the 7 grains of oxygen, the original weight. Hence we have 39 grains of the oxide resolved into 32 protoxide, and 7 oxygen. If then we allow 32 protoxide, to contain 7 oxygen, it appears that 39 grains of the native oxide, consists of 1 atom manganese (25), and two atoms of oxygen (14); or it is the deutoxide of the metal. 2d. A more direct and expeditious method, of transferring the oxygen from the manganese to the iron, is as follows: Let 39 grains of pure grey shining oxide, be mixed with 800 of test green sulphate of iron; to this mixture let 25 or 30 grain measures of strong sulphuric acid be added: after stirring the mixture for 5 minutes, the oxide of manganese will be completely dissolved, and, on precipitating the oxide of iron gradually, by lime water, it will be found to be wholly yellow or buff; shewing that 7 grains of oxygen have been transferred from the oxide of manganese to that of iron.—If more green sulphate of iron be used, then the surplus of the oxide will be thrown down green; the order of precipitation being the yellow oxide of iron, the green oxide of iron, and lastly, the yellow or buff oxide of manganese, as has been stated. This affords an easy and elegant method of appreciating the different oxides of manganese of commerce; and it was in this mode, the valuations of the specimens in the above table were made.

The proportions of the three oxides are then as under:

Manganese Oxygen

Protoxide 100 + 28 — buff; soluble in acids.

Intermediate oxide — + 42 — brown; insoluble.

Deutoxide — + 56 — black; insoluble.

It may be proper to subjoin the results of others, who have investigated the oxides of manganese. Bergman finds 3 oxides, containing 100 metal + 25, 35, and 66.6 oxygen; Dr. John finds 3 oxides, containing 100 metal + 15, 25, and 40 oxygen: Berzelius finds 5 oxides, containing 100 metal + 7, 14, 28, 42, and 56 oxygen; and Davy finds 2 oxides, containing 100 metal + 26.6, and 39.9 oxygen, respectively.

23. Oxides of chromium.

There appear to be at least two oxides of chromium, one or other of which is found in combination with the oxides of lead or iron, but hitherto so very sparingly that few chemists have had an opportunity of investigating the proportions of chrome and oxygen, in the oxides of chromium. The chief sources for information on this subject, are essays by Vauquelin, An. de Chimie, Vol. 25 and 70; by Tassaert, ibid. 31; by Mussin Puschin, ibid. 32; by Godon, ibid. 53; by Laugier ibid. 78, and by Berzelius, Annal. of Philosophy, 3.

The oxides of chromium, as might be supposed, are distinguished for the colours which they possess and impart to the compounds into which they enter. One of the oxides is green; it gives colour to the emerald. The other is yellow, dissolved in water, but deep red when crystallized, and possesses the characters of an acid; it unites with alkalies, earths, and metallic oxides; it was first found in Siberia, in combination with the oxide of lead, a salt now denominated chromate of lead, of a splendid yellow colour, inclining to orange or red. Since then, the chromate of iron, has been found in France, America, and Siberia, with a prospect of greater abundance.

In order to investigate the weight of the atom of chromic acid, it is necessary to attend to such of the chromates as have been carefully examined. The chromates of potash, barytes, lead, iron, and mercury, are those with which we are best acquainted.

Vauquelin has given us the components of the native chromate of lead by analysis, and those of the artificial chromate by synthesis; the results do not accord very nearly: for, according to the analysis corrected by the modern science,

Chromate of lead = 62 acid + 97 oxide

By synth. chromate of lead = 57½ — + 97 —

Berzelius however, has more lately given us the results of his experience, both analytical, and synthetical; and he finds both to give chromate of lead nearly = 44 acid + 97 oxide.

Chromate of barytes (Vauq.) = 47.8 acid + 68 barytes

Ditto (Berz.) = 44 — + 68 —

Native chromate of iron (Vauq.) = 45 acid + 35½ oxide

Ditto (Laugier) = 55 — + 35½ —

Having received a small portion of chromate of potash in solution, from a chemical friend (J. Sims), I endeavoured to satisfy myself, as far as my materials would go, as to the nature and proportions of the chromates. The solution was of the sp. gr. 1.061, and consequently in 100 measures contained nearly 6.7 grains of chromic acid and potash, &c.—The liquid was a beautiful yellow; it was alkaline by the colour test. By the usual tests, I had reason to believe, that the solution contained as under per cent.—namely,

2.2 gr. chromic acid

2. potash

.8 uncomb. potash

1.4 carb. potash

.3 sulphate of potash

6.7

With this liquid neutralized by nitric acid, I formed the chromates of lead, barytes, iron, and mercury; and I am inclined to believe these salts are nearly constituted as under:

Neutral chromate of potash 46 acid + 42 potash

— — of barytes 46 — + 68 barytes

— — of lead 46 — + 97 oxide

— — of iron 46 — + 32 oxide (black)

— — of mercury 46 — + 174 oxide (black)

According to these results, the atom of chromic acid weighs 46; it is made 44 by the results of Berzelius, and from 45 to 62 by those of Vauquelin; I would not be understood to place great confidence in the above results of mine, though I am persuaded they will be found good approximations.

Is the chromic acid the deutoxide, or the tritoxide of chromium?

The determination will evidently be affected by the question, how much oxygen must be abstracted from the chromic acid to reduce it to the green oxide. Vauquelin finds 46 acid to lose 6½ oxygen, and Berzelius 10½, when converted into green oxide by heat. From the former of these, one would infer chrome to be 32, the green or protoxide of chrome to be 39, and the acid or deutoxide 46: from the latter, chrome = 25, protoxide = 32 (unknown), the green oxide = 1 protoxide and 1 deutoxide united [= 71 = 50 chrome + 21 oxygen = (25 chrome + 10½ oxygen) × 2 = 35½ × 2] the deutoxide = 39, and the tritoxide or chromic acid = 46. I have not had an opportunity to perform any experiment that appears to me decisive as to the accuracy of one or other of these views; but shall make a few remarks relative to them.

The green oxide being the most prominent compound next to the chromic acid, being commonly produced from it by any deoxidizing process, being the lowest oxide known, and combining with acids, is on these accounts entitled to the consideration of the protoxide; indeed there does not seem an instance where the protoxide of a metal is unknown, whilst the deutoxide and compound oxides are known. There is however, another oxide observed by Vauquelin and by Berzelius, which is obtained by heating the nitrate, or combination of nitric acid and the green oxide, to dryness and expelling the acid; this oxide is brown, and gives oxymuriatic acid when treated with muriatic acid; on this account it would seem to be intermediate between the green oxide and the chromic acid; it is probably a combination of the two, or the chromate of chromium. On the other view however, it must be considered as the deutoxide. What corroborates the notion of the green oxide being 39, is the fact which I have observed, of 46 parts of chromic acid combining with 64 of the green oxide of iron to form 110 of chromate of iron; in this combination the oxide of iron may be said to borrow 1 atom of oxygen from the chromic acid, and the compound may then be considered as the union of the green oxide of chrome, and the red oxide of iron. When this precipitate is subjected to the action of muriatic acid, a green solution is obtained containing the oxide of chrome, and red oxide of iron is precipitated, as Vauquelin has observed. To form the above chromate (or rather subchromate) of iron, let a given portion of neutral chromate of potash be treated with green sulphate of iron, and lime water be added, sufficient to saturate the sulphuric acid, a brown red precipitate is obtained; more sulphate and lime water must be gradually added to the clear liquid till the precipitate become green, when the proportions will be found as above stated. This artificial compound seems a subchromate; whereas the native compound seems to be a chromate. That there is some uncertainty in decomposing a chromate by heat with a view to obtain the green oxide, I have reason to suspect from having decomposed 5⅓ grains of chromate of mercury by a moderate red heat; this compound contained 1.1 chromic acid, and it yielded only .6 of green oxide, whereas it should have been .9 or .8 at least.

Upon the whole I think the evidence is in favour of the opinion that the atom of chrome is 32, the green or protoxide 39, and the deutoxide or chromic acid is 46.

24. Oxides of uranium.

There appear to be two oxides of uranium from the experiments of Klaproth, Bucholz, and Vauquelin; but the proportions of metal and oxygen have not been very nearly ascertained, from the great scarcity of the minerals containing this metal. (Vid. Bucholz, An. de Chimie, 56—142. Vauquelin, ibid. 68—277; or Nicholson’s Journ. 25—69). The oxides are obtained by precipitation from solutions of the minerals in the nitric or muriatic acid, the foreign substances being first separated.

The protoxide of uranium precipitates dark bottle green by caustic alkalies, and forms crystallizable salts with acids; the other, probably the deutoxide, precipitates orange yellow, and forms uncrystallizable salts with acids; in these respects the oxides bear a near resemblance to those of iron.

Bucholz estimates the yellow oxide at 100 metal + from 25 to 32 oxygen; as it yields oxymuriatic acid when treated with muriatic, it is most likely to be the deutoxide; now if we take 28 for the oxygen combined with 100 metal, the protoxide must consist of 100 metal + 14 oxygen, or of 50 metal + 7 oxygen, and the atom of uranium = 50. From his account of the sulphate and nitrate of uranium the weight of the atom might be inferred to be double of the above or 100. These different conclusions can only be elucidated by future experiments.

25. Oxides of molybdenum.

The latest and as it should seem most accurate experiments on the oxides of molybdenum were made by Bucholz. (Vid. Nicholson’s Journal, 20, p. 121). There appear to be 3 oxides or combinations of molybdenum and oxygen, namely, the brown, the blue, and the white or yellow. The two last have the character of acids, and none of them seem to form salts with acids, like oxides in general. Bucholz ascertained the above gradation, and that the white oxide or molybdic acid contains ⅓ of its weight of oxygen; (which has since been corroborated by Berzelius); he also found that the blue was best formed by mixing, triturating, and boiling in water 3 parts of brown oxide, and 4 of white, or one of metal, and two of acid; and that it has acid qualities as well as the white. Bucholz also found 3 parts of liquid ammonia of the sp. gr. .97 dissolve 1 of molybdic acid; now 3 parts of ammonia = .186 real (Vol. 1, p. 422); and 1 ∶ .186 ∷ 64 ∶ 12, the quantity of ammonia usually saturated by one atom of acid; and Berzelius found 100 molybdic acid saturate 155 oxide of lead, or 63 acid to 97 oxide. The native sulphuret of molybdenum (the state in which this metal is usually found) was analyzed by Bucholz and found to consist of 60 metal and 40 sulphur.

The molybdic acid may be obtained by roasting the sulphuret in a crucible and stirring it frequently; the sulphur in great part escapes in the form of sulphurous acid and the metal becomes oxidated: carbonate of soda in solution may be added to the residuum as long as any effervescence is observed; molybdate of soda remains in solution and the acid may be precipitated by nitric acid. The brown oxide is best obtained by heating molybdate of ammonia to red; the ammonia and part of the oxygen are expelled, and the brown oxide remains.

There are two views with which the preceding results may be reconciled; namely, 1st. supposing the atom of molybdenum to weigh 21; and 2d, by supposing it to weigh 42 or twice that number. In the first case the brown oxide will weigh 24½ (49) being supposed 2 atoms of metal and 1 of oxygen, the blue or protoxide will weigh 28, and the white oxide or molybdic acid will weigh 63, being a compound of the protoxide and deutoxide, molybdena or native sulphuret will then be as usual, the protosulphuret, consisting of 21 metal and 14 sulphur, or 60 metal and 40 sulphur. In the 2d. case the brown or protoxide will weigh 49, the blue or deutoxide 56, and the acid or tritoxide 63. The native sulphuret, molybdena, must in this view be the deutosulphuret, or 42 metal and 28 sulphur.

The former of these views exhibits the oxides somewhat complicated, but agrees well with the sulphuret; the latter shews the oxides in a more regular train, but does not appear so probable from the sulphuret; besides, the notion of a metallic tritoxide is rather singular, especially in a metal that is rarely if ever found in combination with oxygen. Upon the whole I prefer the former view; but it must be considered as problematical only. The atom of 60 (see page 267 Vol. 1) must doubtless be erroneous.

26. Oxides of tungsten.

From the experiments of D’Elhuiarts, Bucholz[13] and Berzelius[14] it seems very probable that the tungstic acid is composed of about 100 metal + 25 oxygen. It is a yellow powder of the sp. gr. 6.12, and is best obtained from the native tungstate of lime (a scarce mineral). One part tungstate of lime and four of carbonate of potash are fused together, dissolved in water, and then the tungstic acid may be precipitated by nitric acid. There is an inferior oxide that is black or dark brown; Berzelius reduced the yellow oxide to a flea-brown colour, by sending a current of hydrogen gas through it in a glass tube heated red hot. 100 parts of this oxide burnt be 107 yellow oxide. Hence 100 metal must combine with about 16½ or 17 oxygen to form this oxide, which is ⅔ of that in the yellow or tungstic acid.—Upon the whole it does not seem improbable, considering the great sp. gravity of this metal, that it forms three oxides and that the acid or yellow oxide is the 3d. Hence the atom of tungsten must be 84, that of the protoxide 91, the deutoxide 98, and the tritoxide or tungstic acid 105. The native tungstate of lime, if pure, according to this would be 81.4 acid + 18.6 lime, which is not far from Klaproth’s analysis; he having found 18.7 lime in one specimen; nor from that of Berzelius, he having found 80.4 tungstic acid and 19.4 lime in 99.8 tungstate of lime.[15]

There is another view however, which would accord with the experiments and perhaps will be found preferable in other respects; that is, to suppose the tungstic acid to be composed of 1 atom deutoxide and 1 atom protoxide united; in this case the atom of tungsten = 42, that of the protoxide = 49, that of the deutoxide = 56, and the tungstic acid = 105 as before.

27. Oxides of titanium.

Nothing certain is known respecting the oxides of titanium. An observation of Richter, quoted by Berzelius (An. of Philos. 3—251), if it could be relied upon, furnishes an important fact, namely, that a solution of muriate of titanium containing 84.4 oxide, gave 150 muriate of silver. Now 150 muriate of silver contain 28 acid; hence 28 acid must have combined with 84.4 oxide; but if 28 ∶ 84.4 ∷ 22 ∶ 66 nearly for the weight of an atom of the oxide. This would indicate 59 for an atom of the metal.

28. Oxides of columbium.

The white oxide or acid of columbium is found in combination with the oxides of iron and manganese in proportion nearly as 4 of the acid to 1 of the aggregate oxides. The two minerals, columbite and tantalite, though yielding these substances nearly in the same proportions, are found to differ remarkably in specific gravity, the former being about 5.9 and the latter about 7.9. Dr. Wollaston concludes however, from the agreement of the white oxides extracted, that they must be the same. The white oxide of columbium is insoluble in the mineral acids; it unites with potash by fusion, and may be precipitated by most acids. Some of the vegetable acids, the oxalic, the tartaric, and the citric dissolve the white oxide. When the alkaline solution of columbium previously neutralized by an acid is treated with infusion of galls, an orange precipitate is produced which is characteristic of columbium. Nothing certain has been determined respecting the proportions of metal and oxygen; but from the great proportion of the columbic acid found with the oxides of iron and manganese, together with the great sp. gravity of the compound, one may pretty clearly infer the great weight of the atom of columbium. Supposing the white oxide or acid to consist of 1 atom metal + 3 oxygen and that the columbite is formed by 1 atom of acid to 1 of oxide, we should have 128 acid + 32 oxide. This would give 107 for the weight of an atom of metal, and 128 for that of the tritoxide or columbic acid; but it is unnecessary to dwell upon such conjectures.

In a recent memoir of Messrs. Gahn, Berzelius, and Eggertz (An. de Chimie, Octo. 1816), it is maintained as probable that there is only one oxide of columbium or tantalum, and that 100 metal take 5.485 oxygen, or 121 metal take 7 oxygen. If this be correct, the atom of columbium must be 121 and the protoxide 128.

(See also An. de Chimie, 43—271; Philos. Trans. 1802; Nichols. Journ. 2—129; ibid. 3—251; ibid. 25—23).

29. Oxides of cerium.

The mineral cerite is of the sp. gr. 4.53, and constituted of 50 or 60 per cent. of oxide of cerium, with silex, lime, and iron. This mineral being calcined and dissolved in nitro-muriatic acid, the solution is to be neutralized by caustic potash, and then treated with tartrate of potash. The precipitate, well washed and afterwards calcined, is pure oxide of cerium. This oxide, which is white, when calcined in the open air becomes red and acquires more oxygen. These oxides, particularly the white, are soluble in most acids; the red oxide with muriatic acid gives oxymuriatic acid.

The experiments hitherto made on this subject scarcely enable us to decide respecting the proportions of metal and oxygen, nor the relative weights of these oxides.

Both Vauquelin[16] and Hisinger[17] agree that the protocarbonate of cerium, when exposed to a red heat, yields 57 or 58 oxide, which the former says is the red oxide, being changed by the calcination. Hisinger finds the percarbonate to consist of 36.2 acid and 63.8 oxide: also that the muriate of cerium consists of 100 acid and 197.5 oxide; but Vauquelin remarks that the sulphate, nitrate, and muriate of cerium are always more or less acid, however dried; and he found the protoxalate of cerium to yield 45.6 red oxide by calcination, on a mean of 3 experiments not much differing from each other. Supposing all these facts accurate, they may be reconciled by a few suppositions by no means improbable. Let the atom of cerium be 22, the protoxide 29, and the red oxide 32½ (that is, 1 oxy. + 2 protox. = 65); and let the protocarbonate be 1 atom of acid, 1 of oxide, and 1 of water; the percarbonate, 1 acid 1 oxide; the oxalate, 1 acid (40) and 1 oxide; and the muriate, saturated with base, 3 oxide and 2 acid. Then it will be found that,

The decomposed protocarbonate will yield 57.5 red oxide;

The decomposed percarbonate will yield, 36.7 acid, 63.3 oxide;

The decomposed oxalate will yield 47 red oxide; and

The muriate will yield 100 acid (22), and 197.7 oxide.

All of which agree very nearly with the results above obtained.

Hence it appears to me very probable that the several atoms of the metal and the oxides are as stated above; and that,

100 cerium + 31.8 oxygen = 131.8 protoxide, white.

——— + 47.7 —— = 147.7 intermediate, red.

Hisinsger, from some of the same data united to other hypothetical facts than those assumed above, deduces the two oxides very different; viz. 100 metal + 17.4 oxygen for the protoxide, and 100 + 26.1 for the peroxide.