Note 36 — Chapter XIX · PHOSPHORUS AND THE OTHER ELEMENTS OF THE FIFTH GROUP

Arsenious anhydride is obtained in an amorphous form after prolonged heating at a temperature near to that at which it volatilises, or, better still, by heating it in a closed vessel. It then fuses to a colourless liquid, which on cooling forms a transparent vitreous mass, whose specific gravity is only slightly less than that of the crystalline anhydride. On cooling, this vitreous mass undergoes an internal change, in which it crystallises and becomes opaque, and acquires the appearance of porcelain. The following difference between the vitreous and opaque varieties is very remarkable: when the vitreous variety is dissolved in strong and hot hydrochloric acid it gives crystals of the anhydride on cooling, and this crystallisation is accompanied by the emission of light (which is visible in the dark), and the entire liquid glows as the crystals begin to separate. The opaque variety does not emit light when the crystals separate from its hydrochloric acid solution. It is also remarkable that the vitreous variety passes into the opaque form when it is pounded—that is, under the action of a series of blows. Thus, several varieties of arsenious anhydride are known, but as yet they are not characterised by any special chemical distinctions, and even differ but little in their specific gravities, so that it cannot be said that the above differences are due to any isomeric transformation—that is, to an arrangement of the atoms in the molecule—but probably only depend on a difference in the distribution of the molecules, or, in other terms, are physical and not chemical variations. One part of the vitreous anhydride requires twelve parts of boiling water for its solution, or twenty-five parts at the ordinary temperature. The opaque variety is less soluble, and at the ordinary temperature requires about seventy parts of water for its solution.