Note 32 — Chapter XXIV · COPPER, SILVER, AND GOLD

The formation of the alloys Cu + Zn, Cu + Sn, Cu + Bi, Cu + Sb, Pb + Sb, Ag + Pb, Ag + Sn, Au + Zn, Au + Sn, &c., is accompanied by a contraction (and evolution of heat). The formation of the alloys Fe + Sb, Fe + Pb, Cu + Pb, Pb + Sn, Pb + Sb, Zn + Sb, Ag + Cu, Au + Cu, Au + Pb, takes place with a certain increase in volume. With regard to the alloys of gold, it may be mentioned that gold is only slightly dissolved by mercury (about 0·06 p.c., Dudley, 1890); the remaining portion forms a granular alloy, whose composition has not been definitely determined. Aluminium (and silicon) also have the capacity of forming alloys with gold. The presence of a small amount of aluminium lowers the melting point of gold considerably (Roberts-Austen, 1892); thus the addition of 4 p.c. of aluminium lowers it by 14°·28, the addition of 10 p.c. Al by 41°·7. The latter alloy is white. The alloy AuAl2 has a characteristic purple colour, and its melting point is 32°·5 above that of gold, which shows it to be a definite compound of the two metals. The melting points of alloys richer in Al gradually fall to 660°—that is, below that of aluminium (665°).

Heycock and Neville (1892), in studying the triple alloys of Au, Cd, and Sn, observed a tendency in the gold to give compounds with Cd, and by sealing a mixture of Au and Cd in a tube, from which the air had been exhausted, and heating it, they obtained a grey crystalline brittle definite alloy AuCd.