Note 26 bis — Chapter XXII · IRON, COBALT, AND NICKEL

When Mond and his assistants obtained the remarkable volatile compound Ni(CO)4 (described later, Chapter XXII.), it was shown subsequently by Mond and Quincke (1891), and also by Berthelot, that iron, under certain conditions, in a stream of carbonic oxide, also volatilises and forms a compound like that given by nickel. Roscoe and Scudder then showed that when water gas is passed through and kept under pressure (8 atmospheres) in iron vessels a portion of the iron volatilises from the sides of the vessel, and that when the gas is burnt it deposits a certain amount of oxides of iron (the same result is obtained with ordinary coal gas which contains a small amount of CO). To obtain the volatile compound of iron with carbonic oxide, Mond prepared a finely divided iron by heating the oxalate in a stream of hydrogen, and after cooling it to 80°-45° he passed CO over the powder. The iron then formed (although very slowly) a volatile compound containing Fe(CO)5 (as though it answered to a very high type, FeX10), which when cooled condenses into a liquid (slightly coloured, probably owing to incipient decomposition), sp. gr. 1·47, which solidifies at -21°, boils at about 103°, and has a vapour density (about 6·5 with respect to air) corresponding to the above formula; it decomposes at 180°. Water and dilute acids do not act upon it, but it decomposes under the action of light and forms a hard, non-volatile crystalline yellow compound Fe2(CO)7 which decomposes at 80° and again forms Fe(CO)5.