Note 21 — Chapter XVII · BORON, ALUMINIUM, AND THE ANALOGOUS METALS OF THE THIRD GROUP

The treatment of bauxite is carried on on a large scale, chiefly in order to obtain alumina from alkaline solutions, free from ferric oxide, because in dyeing it is necessary to have salts of aluminium which do not contain iron. But this end, it would seem, may also be obtained by igniting alumina containing ferric oxide in a stream of chlorine mixed with hydrocarbon vapours, as ferric chloride then volatilises. K. Bayer observed that in the treatment of bauxite with soda, about 4 molecules of sodium hydroxide pass into solution to 1 molecule of alumina, and that on agitating this solution (especially in the presence of some already precipitated aluminium hydroxide), about two-thirds of the alumina is precipitated, so that only 1 molecule of alumina to 12 molecules of sodium hydroxide remains in solution. This solution is evaporated directly, and used again. He therefore treats bauxite directly with a solution of NaHO at 170° in a closed boiler, and on cooling adds hydrated alumina to the resultant solution. The greater part of the dissolved alumina then precipitates on this hydrated alumina, and the solution is used over again. The hydroxide which separates from the alkaline solution contains Al(OH)3. All these properties bear a great resemblance to those of boric acid. It may be taken for granted that the relation between sodium hydroxide and alumina in solution varies with the mass of water.

If lime be added to a solution of alumina in alkali (sodium aluminate) calcium aluminate is precipitated, from which acids first extract the lime, leaving aluminium hydroxide, which is easily soluble in acids (Loewig). When sodium aluminate is mixed with a solution of sodium bicarbonate, a double carbonate of the alkali and aluminium is precipitated, which is easily soluble in acids.