Note 18 bis — Chapter XVII · BORON, ALUMINIUM, AND THE ANALOGOUS METALS OF THE THIRD GROUP

Frémy (1890) obtained transparent rubies, which crystallised in rhombohedra, and resembled natural rubies in their hardness, colour, size, and other properties. He heated together a mixture of anhydrous alumina containing more or less caustic potash, with barium fluoride and bichromate of potassium. The latter is added to give the ruby its colour, and is taken in small quantity (not more than 4 parts by weight to 100 parts of alumina). The mixture is put into a clay crucible, and heated (for from 100 hours to 8 days) in a reverberatory furnace at a temperature approaching 1,500°. At the end of the experiment the crucible was found to contain a crystalline mass, and the walls were covered with crystals of the ruby of a beautiful rose colour. It was found that the access of moist air was indispensable for the reaction. According to Frémy, the formation of the ruby may be here explained by the formation of fluoride of aluminium which under the action of the moist air at the high temperature of the furnace gives the ruby and hydrofluoric acid gas.