Note 10 — Chapter XVII · BORON, ALUMINIUM, AND THE ANALOGOUS METALS OF THE THIRD GROUP

Amorphous boron is prepared by mixing 100 parts of powdered boric anhydride with 50 parts of sodium in small lumps; this mixture is thrown into a powerfully heated cast-iron crucible, covered with a layer of ignited salt, and the crucible covered. Reaction proceeds rapidly; the mass is stirred with an iron rod, and poured directly into water containing hydrochloric acid. The action is naturally accompanied by the formation of sodium borate, which is dissolved, together with the salt, by the water, whilst the boron settles at the bottom of the vessel as an insoluble powder. It is washed in water, and dried at the ordinary temperature. Magnesium, and even charcoal and phosphorus, are also able to reduce boron from its oxide. Boron, in the form of an amorphous powder, very easily passes through filter-paper, remains suspended in water, and colours it brown, so that it appears to be soluble in water. Sulphur precipitated from solutions shows the same (colloidal) property. When borax is fused with magnesium powder, it gives a brown powder of a compound of boron and magnesium, Mg2B (Winkler, 1890), but when a mixture of 1 part of magnesium and 3 parts of B2O3 is heated to redness (Moissan, 1892), it forms amorphous boron in the form of a chestnut-coloured powder, which, after being washed with water, hydrochloric and hydrofluoric acids, is fused again with B2O3 in an atmosphere of hydrogen in order to prevent the access of the nitrogen of the air, which is easily absorbed by incandescent amorphous boron.

Sabatier (1891) considers that a certain amount of gaseous hydride of boron is evolved in the action of hydrochloric acid upon the alloys of magnesium and boron, because the gas disengaged burns with a green flame. Still, the existence of hydride of boron cannot be regarded as certain.

Under the action of the heat of the electric furnace boron forms with carbon a carbide, BC, as Mühlhäuser and Moissan showed in 1893.