Note 1 — Chapter XVII · BORON, ALUMINIUM, AND THE ANALOGOUS METALS OF THE THIRD GROUP

Borax is either directly obtained from lakes (the American lakes give about 2,000 tons and the lakes of Thibet about 1,000 tons per annum), or by heating native calcium borate (see Note 2) with sodium carbonate (about 4,000 tons per annum), or it is obtained (up to 2,000 tons) from the Tuscan impure boric acid and sodium carbonate (carbonic anhydride is evolved). Borax gives supersaturated solutions with comparative ease (Gernez), from which it crystallises, both at the ordinary and higher temperatures, in octahedra, containing Na2B4O7,5H2O. Its sp. gr. is 1·81. But if the crystallisation proceeds in open vessels, then at temperatures below 56°, the ordinary prismatic crystallo-hydrate B4Na2O7,10H2O is obtained. Its sp. gr. is 1·71, it effloresces in dry air at the ordinary temperature, and at 0° 100 parts of water dissolve about 8 parts of this crystallo-hydrate, at 50° 27 parts, and at 100° 201 parts. Borax fuses when heated, loses its water and gives an anhydrous salt which at a red heat fuses into a mobile liquid and solidifies into a transparent amorphous glass (sp. gr. 2·37), which before hardening acquires the pasty condition peculiar to common molten glass. Molten borax dissolves many oxides and on solidifying acquires characteristic tints with the different oxides; thus oxide of cobalt gives a dark blue glass, nickel a yellow, chromium a green, manganese an amethyst, uranium a bright yellow, &c. Owing to its fusibility and property of dissolving oxides, borax is employed in soldering and brazing metals. Borax frequently enters into the composition of strass and fusible glasses.